Casting & Tooling Systems
|
RESINS
ARE LISTED WITH MOST POPULAR HARDENER. HOWEVER,
WE HAVE MANY OTHER HARDENERS WHICH ALLOW FOR INDIVIDUAL
PRODUCT DESIGN.
|
| Uni-Cast M.C.
w/hardener 210 is
iron-filled abrasion resistant compounds used where heavy section
casting is required. With a slow cure, they are very stable
products with negligible shrinkage, excellent heat dissipation
and a low coefficient of expansion. |
POT LIFE
minutes
(100 gram Mass) |
MAXIMUM USE
TEMPERATURE
°F |
HARDNESS
SHORE "D"
@ 72°F |
MIXING RATIO
(Parts by Weight)
RESIN/HARDENER |
MIXED
VISCOSITY
cps @ 72°F |
COMPRESSIVE
STRENGTH
PSI |
FLEXURAL
STRENGTH
PSI |
TENSILE
STRENGTH
PSI |
CTE
In/In/°F
x 10-5 |
| 120 |
250 |
85 |
100/7 |
14,350 |
29,000 |
8,500 |
7,200 |
2.10 |
| Uni-Cast A.S.C.T.
w/hardener 601 is a gray, aluminum filled surface casting
resin that is virtually indestructible. It produces a hard,
durable casting, and allows for extremely accurate reproductions.
It is a safe, low odor system especially designed to cast in
sections of 1/64" to 1/2" in thickness. |
| 80 |
250 |
80 |
100/18 |
16,000 |
17,200 |
10,200 |
8,100 |
2.90 |
|
Uni-Cast M.S. w/hardener
215 is a very hard, glass corundum filled material
used where high impact and abrasion resistance is required.
The material has excellent dimensional stability with thermal
and mechanical shock properties. The material can be cast
up to 1" thick against metal surfaces and cures with
low exotherms.
|
| 90 |
250 |
90 |
100/15 |
8,000 |
38,000 |
20,500 |
9,600 |
3.70 |
|
E-Cast F-28 w/hardener
UCE-302 is an unfilled, low viscosity casting system.
This system offers excellent air release that is used where
clarity is needed. This system has excellent UV stability.
|
| 10-12 hrs. |
200 |
85 |
100/36 |
700 |
25,700 |
14,500 |
8,300 |
– |
| E-Cast F-28 w/hardener
213 provides high heat deflection temperatures coupled
with excellent mechanical, chemical, and electrical properties.
Formulated for low thermal expansion and excellent impact resistance.
Meets Mil Spec. MIL-C-47257C. Ideal for filament winding and
a post heat cure. |
POT LIFE
minutes
(100 gram Mass) |
MAXIMUM USE
TEMPERATURE
°F |
HARDNESS
SHORE "D"
@ 72°F |
MIXING RATIO
(Parts by Weight)
RESIN/HARDENER |
MIXED
VISCOSITY
cps @ 72°F |
COMPRESSIVE
STRENGTH
PSI |
FLEXURAL
STRENGTH
PSI |
TENSILE
STRENGTH
PSI |
CTE
In/In/°F
x 10-5 |
| 24 hrs. |
400 |
85 |
100/80 |
2,500 |
25,000 |
14,500 |
6,000 |
2.23 |
| Tooling Foam
is a light weight, non-expanding/non-shrinking epoxy compound.
It is color coded to insure proper mixing. Due to its consistency,
it is easily packed onto the duplicating surface. When used
with fiberglass cloth in a sandwich panel construction, it exhibits
excellent dimensional stability and strength. Approved for use
in the aerospace, automotive, marine and recreational vehicle
industries. |
| 50 |
250 |
55 |
100/33 |
Syntatic Dough |
28,000 |
32,000 |
500 |
2.44 |
|
Styling Foam is
a light weight, non-expanding epoxy compound developed for medium-temperature
performance. Styling Foam has excellent machinability. It
is easily sanded and shaped.
|
| 120 |
250 |
60 |
100/50 or 100 |
Syntatic Dough |
13,500 |
5,900 |
500 |
2.11 |
|
Epoxy Molding Compound
is light-weight, durable molding material that is color coded
to insure proper mixing. Its low exotherm during cure offers
high dimensional stability making it ideal for structural
applications.
|
| 180-240 |
250 |
72 |
100/100 |
Paste |
5,100 |
4,550 |
8,850 |
2.34 |
|
Marine Fairing Compound
is a light weight faring compound. Ideal for filling, fairing
and patching large areas on various substrates. Sprayable
coating is available to obtain a minimal porosity. This material
provides superior flexibility over conventional systems. Its
low exotherm during cure allows for minimal porosity on the
finished surface after cure.
|
Reg. 2-3 hrs
Fast 30 min |
250
250 |
70
75 |
100/100
100/100 |
Paste
Paste |
20,000
20,000 |
12,000
12,000 |
610
610 |
2.11
2.11 |
|
|