Surface Coating & Laminating Systems
|
RESINS
ARE LISTED WITH MOST POPULAR HARDENER. HOWEVER,
WE HAVE MANY OTHER HARDENERS WHICH ALLOW FOR INDIVIDUAL
PRODUCT DESIGN.
|
| Uni-Gel
S.C. 90 w/hardener TP-41F is a white, room temperature cure,
epoxy surface coat. It has good bonding properties, holds well on
vertical surfaces and its viscosity allows it to be easily measured
through a dispenser. It is highly recommended for plastic faced plasters
and renders a hard surface. This system is also available in a thin
version suitable for spray applications. |
POT LIFE
minutes
(100 gram Mass) |
MAXIMUM USE
TEMPERATURE
°F |
HARDNESS
SHORE "D"
@ 72°F |
MIXING RATIO
(Parts by Weight)
RESIN/HARDENER |
MIXED
VISCOSITY
cps @ 72°F |
COMPRESSIVE
STRENGTH
PSI |
FLEXURAL
STRENGTH
PSI |
TENSILE
STRENGTH
PSI |
CTE
In/In/°F
x 10-5 |
| 20 |
250 |
90 |
100/14 |
170,000/
18,000 (thin)
|
16,800 |
7,000 |
5,100 |
4.8 |
| High Heat Surface Coat
w/hardener 118 and hardener 203 are aluminum filled high heat
surface coats used as a base on high heat tools. Designed to produce
void free duplications that are dimensionally accurate. The system
demonstrates high surface strength with superior physical properties.
Post curing is required to obtain maximum deflection temperatures. |
70
240 |
400
400 |
85
85 |
100/11
100/13 |
25,350
25,350
|
26,500
26,500 |
7,950
7,950 |
4,000
4,000
|
2.3
2.3 |
| Uni-Lam RTL w/hardener
PT-60F is a room temperature curing system,
with excellent dimensional stability. It has excellent wet-out qualities
when laminating with glass cloth. The material will not sag on the
vertical surfaces, nor will it shrink. It is approved for automotive
and aerospace applications. |
POT LIFE
minutes
(100 gram Mass) |
MAXIMUM USE
TEMPERATURE
°F |
HARDNESS
SHORE "D"
@ 72°F |
MIXING RATIO
(Parts by Weight)
RESIN/HARDENER |
MIXED
VISCOSITY
cps @ 72°F |
COMPRESSIVE
STRENGTH
PSI |
FLEXURAL
STRENGTH
PSI |
TENSILE
STRENGTH
PSI |
CTE
In/In/°F
x 10-5 |
| 35 |
250 |
85 |
100/20 |
3,000 |
40,000 |
29,443 |
5,500 |
1.48 |
| Uni-Lam 1069 w/hardener
PT-60F is a room temperature laminating system
with good dimensional stability. It has good wet-out qualities. The
material will not sag on vertical surfaces. |
| 35 |
250 |
85 |
100/15 |
8,800 |
38,000 |
32,000 |
5,500 |
1.8 |
|
Uni-Lam HHL w/hardener 118 and
hardener 203 are high heat laminating systems especially
designed for tools that require high temperature exposure. This
material works well with vacuum bag construction. It cures at room
temperature or can be heat cycle cured. Post curing is required
to obtain maximum deflection temperatures.
|
50
240 |
370
370 |
90
90 |
100/15
100/17 |
4,800
3,500 |
39,500
39,500
|
36,800
36,800 |
8,500
8,500 |
1.46
1.46 |
|
Uni-Heat w/hardener 118 and hardener
203 are high heat laminating systems especially designed
for most high temperature tooling applications. It also works well
where vacuum bag construction is used. It cures at room temperature
or can be heat cycle cured. Post curing is required to obtain maximum
deflection temperatures. Uni-Heat w/118 meets MIL Spec. MIL-S-83430A
|
60
180
|
350
500 |
90
90 |
100/20
100/30 |
1,900
1,850 |
40,500
40,500 |
35,600
35,600 |
8,000
8,500 |
0.90
0.92 |
|
Uni-Bond W.G. w/hardener 601
is a clear, unfilled, multi-purpose lamination material which exhibits
excellent moisture and chemical resistance. It has numerous adhesive
applications, including extensive use in the automotive and aerospace
industries as "impreg glue".
|
| 90 |
250 |
85 |
100/33 |
1,445 |
20,000 |
39,900 |
4,000 |
2.90 |
|
Uni-Bond 1070 w/hardener 601
is a unfilled room temperature laminating system with low exotherm.
It is a dimensionally stable material with high surface strength
and a long pot life. This material contains a tracer dye to insure
proper mixing.
|
| 90 |
250 |
85 |
100/33 |
1,445 |
26,500 |
39,000 |
6,300 |
2.10 |
|